Characterization and performance of glass-ceramic sealant to join metallic interconnects to YSZ and anode-supported-electrolyte in planar SOFCs
Smeacetto, F.; Salvo, M.; Ferraris, A.; Casalegno, V.; Asinari, P.; Chrysanthou, A. (2008-09)This work describes the design, development and performance of a glass-ceramic sealant used to join the ceramic electrolyte (YSZ wafer and anode-supported-electrolyte (ASE)) to the metallic interconnects (Crofer22 APU and ... -
Glass-ceramic sealant for solid oxide fuel cells application: Characterization and performance in dual atmosphere
Sabato, A. G.; Cempura, G.; Montinaro, D.; Chrysanthou, A.; Salvo, M.; Bernardo, E.; Secco, M.; Smeacetto, F. (2016-10-01)Glass-ceramic composition was designed and tested for use as a sealant in solid oxide fuel cell (SOFC) planar stack design. The crystallization behaviour was investigated by calculating the Avrami parameter (n) and the ... -
Performance and testing of glass-ceramic sealant used to join anode-supported-electrolyte to Crofer22APU in planar solid oxide fuel cells
Smeacetto, F.; Chrysanthou, A.; Salvo, M.; Zhang, Z.; Ferraris, M. (2009)This work describes the performance and testing of a glass-ceramic sealant used to join the ceramic electrolyte (anode-supported-electrolyte (ASE)) to the metallic interconnect (Crofer22APU) in planar SOFC stacks. The ... -
Thermal cycling and ageing of a glass-ceramic sealant for planar SOFCs
Smeacetto, F.; Chrysanthou, A.; Salvo, M.; Moskalewicz, T.; Bytner, F. D'Herin; Ajitdoss, L. C.; Ferraris, M. (2011-09)Thermal cycling and thermal ageing tests were performed on Crofer22APU/glass-ceramic/Anode-Supported-Electrolyte (ASE) joined samples in air at the SOFC operating temperature of 800 degrees C. The Crofer22APU had been ... -
Thermal cycling of Crofer22APU-sealant-anode supported electrolyte joined structures for planar SOFCs up to 3000 h
Smeacetto, F.; Salvo, M.; Chrysanthou, A.; Moskalewicz, T. (2013)Thermal cyclic tests in air were performed for Crofer22APU/glass-ceramic/ Anode-Supported-Electrolyte (ASE) joined samples for a total period of 3000 h. Different cooling rates from the SOFC operating temperature of 800 C ...