Hu, Zhiqing, Zheng, Huihui, Liu, Guojun and Wu, Hongwei (2018) Effects of Cryogenic Treatment after Annealing of Ti-6Al-4V Alloy Sheet on Its Formability at Room Temperature. Metals, 8 (5): 295.
Copy

In this article, the effects of cryogenic treatment after annealing on the formability of Ti-6Al-4V alloy sheet were experimentally studied. The Ti-6Al-4V titanium alloy was treated by cryogenic treatment after annealing (ACT). Tensile tests were carried out using a universal machine at room temperature. The microstructure evolution of Ti-6Al-4V subjected to ACT was also investigated using an optical microscope (OM). Both the shearing performance and drawing formability were analyzed by punch shearing tests and deep drawing tests, respectively. Results showed that after ACT, the tendency of the β phase can be apparently changing into stable β’ and α’ phases. The elastic modulus is lower than that of the untreated material. It was found that both the yield strength and tensile strength are declined slightly, whereas the ductility is increased significantly. The shear strength in punch shearing is decreased at room temperature and cryogenic temperature. The ratio of smooth zone on the section after ACT3 is much larger than the others. The rollover diameters are not obviously greater than those of the untreated. Additionally, the height of the burr shows a decreasing trend after ACT. During deep drawing, drawing depth is deeper than that of the untreated material, the drawing load after ACT is reduced, and the decreasing tendency of the drawing load slows down. It is noted that the micro-cracks occur at the bottom of the sample.

visibility_off picture_as_pdf

picture_as_pdf
Accepted_Manuscript.pdf
subject
Submitted Version
lock
Restricted to Repository staff only

Request Copy
picture_as_pdf

Published Version


Atom BibTeX OpenURL ContextObject in Span OpenURL ContextObject Dublin Core MPEG-21 DIDL Data Cite XML EndNote HTML Citation METS MODS RIOXX2 XML Reference Manager Refer ASCII Citation
Export

Downloads